TotalEnergies MULTIS COMPLEX SHD 32 – Synthetic Lithium Complex Grease Based on PAO

MULTIS COMPLEX SHD 32 is a synthetic lithium complex grease based on PAO, designed for industrial applications under the toughest conditions. It is developed for heavily loaded bearings operating at medium to high speeds, offering excellent water resistance and reliable lubrication in a wide temperature range from –50 °C to +160 °C. It is ideal where conventional lithium or lithium complex greases are insufficient.

Product Advantages
• Meets lubrication requirements of various equipment and users
• Improved oxidation resistance for extended service life
• Excellent adhesion and high-pressure (EP) performance
• Enhanced protection against false brinelling
• Very good rust and corrosion resistance
• Reduced wear even under heavy load
• Outstanding pumpability at low temperatures
• Contains no lead or other harmful heavy metals

Typical Applications
• Bearings under heavy load at medium to high speed
• Applications requiring high water resistance
• Industrial equipment operating under severe conditions

Specifications/Approvals

ISO 6743-9: L-XEEHB 2
DIN 51502: KP2P-50
Approval: ZAE Drive Systems

Typical Properties
Colour: yellow
NLGI grade: 2
Base oil viscosity at 40 °C (ASTM D445): 32 mm²/s
Dropping point (IP 396): >280 °C
Steel corrosion protection (ASTM D665 A): passed
Penetration at –40 °C (ISO 13737): >160 (0.1 mm)
Consistency change after 100,000 strokes (ASTM D217): 23 (0.1 mm)
Penetration at 25 °C (ASTM D217): 265–295 (0.1 mm)
Operating temperature range: –50 °C to +160 °C
VKA Load-Wear-Index (ASTM D2596): >315 kgf
VKA wear (DIN 51350-5): 0.61 mm
Low-temperature torque at –54 °C start (ASTM D1478): 383 mNm
Low-temperature torque at –54 °C run (ASTM D1478): 51 mNm